AS1701高導熱矽膠 High Thermal Transfer
FEATURE(產品簡介)
- UL94V0 APPROVED UL FILE NO. E334038
- NON-CORROSIVE
- EXCELLENT ADHESION TO MOST SUBSTRATES
- FAST SKINNING
DESCRIPTION(產品簡介)
1 PART RTV SILICONE ADHESIVE SEALANT PASTE NON CORROSIVE UL APPROVED
參數表PARAMETERS
- CODE
AS1701
- FEATURE 1
UL94V0 approved UL file No. E334038
- FEATURE 2
Non-corrosive
- FEATURE 3
Excellent adhesion to most substrates
- FEATURE 4
Fast skinning
- APPEARANCE
Black paste
- TEST CONDITIONS
After 7 days cure at 23°+/-2°C and 50+/-5% humidity
- COLOUR
Black
- SG
1.28
- MIN WORKING TEMP - °C
-50°C
- MAX WORKING TEMP +°C
220 °C
- FDA
NO
- SHELF LIFE
12mths
- MIN STORAGE TEMPERATURE °C
-5 °C
- MAX STORAGE TEMPERATURE °C
+ 40°C
- PACK TYPE
1-PART
- RHEOLOGY
Paste
- TEAR KN/M
19.1 kN/m
- EXTRUSION RATE G/MIN
260 g/min
- NON CORROSIVE
YES
- CURE TYPE
Alkoxy
- RTV OR HEAT CURE
RTV
- SELF BONDING
Yes
- UL 94V-0
Yes
- DURO SHORE A
52
- Tensile MPa
2.35MPa
- ELONGATION %
70 %
- MODULUS YOUNGS MPA
1.8 MPa
- MODULUS @ 100% STRAIN MPA
2.1 MPa
- LINEAR SHRINKAGE %
1 %
- CTE VOLUMETRIC PPM/°C
690ppm/°C
- CTE LINEAR PPM/°C
230 ppm/°C
- TACK FREE TIME MINS
3mins
- SURFACE RESISTIVITY OHMS
3.8E+16 ohms
- THERMAL CONDUCTIVITY W/MK
0.6 W/mK
- VOLUME RESISTIVITY OHMS CM
7.85E+15 ohms cm
- DIELECTRIC CONSTANT @ 1KHZ
2.92
- DIELETRIC STRENGTH KV/MM
>18 kV/mm
- DISSIPATION FACTOR @ 1KHZ
0.0012
- MAX CURE MINS @ 25 °C
24hrs
- DIELECTRIC BREAKDOWN VOLTAGE KV
33kv
- LAP SHEAR COPPER KG/CM²
10.06 kg/cm²
- LAP SHEAR ALUMINIUM KG/CM²
10.78 kg/cm²
- LAP SHEAR STAINLESS STEEL 304 KG/CM²
9.29 kg/cm²
- LAP SHEAR POLYCARBONATE STEEL KG/CM²
5.93 kg/cm²